Manufacturing Defects of SSAW Steel Pipe

Views: 0    

1. **Weld Defects:**

- **Incomplete Fusion:** This occurs when the weld metal does not completely fill the space between the pipe edges, leaving gaps that can become points of failure.

- **Porosity:** Caused by gas pockets trapped in the weld, which can weaken the joint.

- **Cracking:** Hot cracking or cold cracking can occur due to rapid cooling, high welding heat input, or material impurities.

- **Undercutting:** Material removal beneath the weld bead, which can reduce the cross-sectional area of the weld and weaken the joint.

- **Spatter:** Small droplets of molten metal that are ejected from the welding arc and adhere to the surface of the pipe.


2. **Shape and Geometry Defects:**

- **Warping:** Uneven heating and cooling can cause the pipe to warp, affecting its straightness and roundness.

- **ovality:** The cross-section of the pipe may not be perfectly circular, which can lead to uneven stresses on the pipe during operation.

- **Taper:** The diameter of the pipe may not be uniform along its length, causing a taper that can affect the structural integrity.


3. **Surface Defects:**

- **Scaling:** Excess oxidation that results in a rough surface texture on the pipe.

- **Pitting:** Small holes or pits on the surface of the pipe, often caused by corrosion or improper cleaning processes.

- **Surface Cracks:** Microscopic or visible cracks on the pipe surface that can grow under operating conditions.


4. **Material Defects:**

- **Inclusions:** Non-metallic particles or slag that are trapped within the steel during the manufacturing process.

- **Segregation:** Uneven distribution of alloying elements within the steel, which can lead to localized weaknesses.

- **Hardenability Issues:** Some steel grades may harden excessively when cooled rapidly, leading to脆 issues and reduced toughness.


5. **Dimensional Tolerance Deviations:**

- **Wall Thickness Variations:** Inconsistent wall thicknesses can lead to uneven stress distribution and potential failure points.

- **Length Tolerance:** Length variations can be an issue if the pipes are not cut to the specified lengths required for a particular project.


6. **Testing and Inspection Defects:**

- **Non-Destructive Testing (NDT) Failures:** Defects that may not be visible but are detected through NDT methods such as ultrasonic or radiographic testing.

- **Hydrostatic Testing Failures:** Pipes that fail to pass hydrostatic tests due to leaks or other structural issues.


HOT PRODUCT

QUICK LINKS

CONTACT US

  Hunan Gaoxing Steel Development Zone, No.1888 Purui South Rd, Wangcheng District,Changsha, Hunan, China

Tel: 0086-0731-88678598

  inquiry@threewaysteel.com

Copyright  2020 Threeway Steel Co.,Ltd. All Rights Reserved
PRODUCT INQUIRY